CryoTool® Light Weight Composite Wear Plates 4X4X13/64
CryoTool® - Cryogeniclly Treated Carbide Overlay Plates Light Weight Hardness 66-68 Rc Service Temperature Up To 400F With Plug Hole (Pack of 10)
- SDS
- TAA Compliant
Welcome. Register now to see your pricing.
Close
CryoTool® - Cryogeniclly Treated Carbide Overlay Plates Light Weight Hardness 66-68 Rc Service Temperature Up To 400F With Plug Hole (Pack of 10)
Protects equipment without the added weight and capacity reduction of standard carbide overlay plates. Lasts up to 13 times longer than standard wearplates so it saves a tremendous amount of maintenance labor. Thin profile even allows it to be formed to contoured surfaces including pipe as small as 2.5" diameter.
Economical Long life extends maintenance intervals to reduce labor expense
Extremely Wear Resistant Lasts up to 13 times longer than AR-400
Lightweight Reduces added weight for hardfacing by 5 times over standard carbide overlay plate
Formable Thin plates can be cut or contoured to small diameters
Surface Hardness: 66-68Rc
ASTM G65 Abrasion Test: 19.1298mm³ vol. loss
Base Plate Thickness: 5/64"
Carbide Hardfacing Thickness: 1/8"
Service Temperature: Up to 400°F/(204°C)
Protects equipment without the added weight and capacity reduction of standard carbide overlay plates. Lasts up to 13 times longer than standard wearplates so it saves a tremendous amount of maintenance labor. Thin profile even allows it to be formed to contoured surfaces including pipe as small as 2.5" diameter.
Economical Long life extends maintenance intervals to reduce labor expense
Extremely Wear Resistant Lasts up to 13 times longer than AR-400
Lightweight Reduces added weight for hardfacing by 5 times over standard carbide overlay plate
Formable Thin plates can be cut or contoured to small diameters
Surface Hardness: 66-68Rc
ASTM G65 Abrasion Test: 19.1298mm³ vol. loss
Base Plate Thickness: 5/64"
Carbide Hardfacing Thickness: 1/8"
Service Temperature: Up to 400°F/(204°C)